- 密度 [g/cm3]: 1.61
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 7.0
- 彎曲模量 [MPa]: 10.479
- 硬度: 109.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in3 | ISO 1183 |
| Water Absorption | 0.060 % @Temperature 23.0 °C | 0.060 % @Temperature 73.4 °F | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.20 mm | 0.0050 in/in @Thickness 0.126 in | 3.2x7.6x12.6mm; ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | 3.2x7.6x12.6mm; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
| Flexural Strength | 236 MPa | 34200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.479 GPa | 1519.9 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.65e+16 ohm-cm | 1.65e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1000 Hz | 3.8 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 28.4 kV/mm @Thickness 1.60 mm, Temperature 23.0 °C | 721 kV/in @Thickness 0.0630 in, Temperature 73.4 °F | 500 V/s in oil; ASTM D149 |
| Dissipation Factor | 0.0080 @Frequency 1000 Hz | 0.0080 @Frequency 1000 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 13.9 μin/in-°F @Temperature 73.4 - 131 °F | ASTM E831 |
| CTE, linear, Transverse to Flow | 30.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 16.7 μin/in-°F @Temperature 73.4 - 131 °F | ASTM E831 |
| Melting Point | 246 °C | 475 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 270 - 295 °C | 518 - 563 °F | |
| Nozzle Temperature | 275 - 300 °C | 527 - 572 °F | |
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | |
| Mold Temperature | 75.0 - 120 °C | 167 - 248 °F | |