- 熔體流動速率 [g/10min]: 30.0
- 缺口沖擊強度: 6.86
- 拉伸強度 [MPa]: 60.8
- 斷裂伸長率 [%]: 97.1
- 彎曲模量 [MPa]: 2.26
- 硬度: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 30 g/10 min @Load 1.20 kg, Temperature 300 °C | 30 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 60.8 MPa @Thickness 3.20 mm | 8820 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Elongation at Break | >= 150 % @Thickness 3.20 mm | >= 150 % @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Flexural Yield Strength | 97.1 MPa @Thickness 3.20 mm | 14100 psi @Thickness 0.126 in | 10mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 3.20 mm | 327 ksi @Thickness 0.126 in | 10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 6.86 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | >= 12.9 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 6.40 mm | 253 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 265 - 280 °C | 509 - 536 °F | Injection Molding |
| Front Barrel Temperature | 265 - 280 °C | 509 - 536 °F | Injection Molding |
| Nozzle Temperature | 265 - 295 °C | 509 - 563 °F | Injection Molding |
| Melt Temperature | 265 - 290 °C | 509 - 554 °F | Injection Molding |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Injection Molding |
| Drying Temperature | 95.0 - 105 °C | 203 - 221 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |