- 熔體流動速率 [g/10min]: 19.0
- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.4
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Viscosity Test | 92 cm3/g | 92 cm3/g | Viscosity number; ISO 307, 1157, 1628 | ||
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 260 °C | 19 g/10 min @Load 4.76 lb, Temperature 500 °F | Calculated from MVR using melt density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.7 % | 2.7 % | ISO 527-1/-2 | ||
| Tensile Modulus | 7.50 GPa | 1090 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 3.50 J/cm2 @Temperature -30.0 °C | 16.7 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 4.00 J/cm2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | <= 1.00 J/cm2 @Temperature -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| <= 1.00 J/cm2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 7200 MPa | 1.04e+6 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 6100 MPa | 885000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0018 @Frequency 100 Hz | 0.0018 @Frequency 100 Hz | IEC 60250 | ||
| 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 μm/m-°C | 22.2 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 70.0 μm/m-°C | 38.9 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 205 °C | 401 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Oxygen Index | 21 % | 21 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 °C | 518 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 90.0 °C | 194 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Additives | Release agent | ||||
| Features | Heat stabilized or stable to heat | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT+PET,GHMR,09-070,GF20 | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||