- 密度 [g/cm3]: 1.51
- 缺口沖擊強度: 0.7
- 彎曲模量 [MPa]: 9.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | ASTM D955 |
| Ash | 30 % | 30 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 140 MPa | 20300 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 190 MPa | 27600 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 9.80 GPa | 1420 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm @Temperature 23.0 °C | 1.31 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | |
| Mold Temperature | 75.0 - 100 °C | 167 - 212 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi | |