- 密度 [g/cm3]: 1.41
- 缺口沖擊強度: 0.55
- 彎曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | ASTM D955 |
| Ash | 15 % | 15 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 130 MPa | 18900 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.550 J/cm @Temperature 23.0 °C | 1.03 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | |
| Mold Temperature | 75.0 - 100 °C | 167 - 212 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi | |