- 密度 [g/cm3]: 1.27
- 缺口沖擊強度: 0.94
- 拉伸強度 [MPa]: 50.0
- 斷裂伸長率 [%]: 72.0
- 彎曲強度 [MPa]: 29.0
- 彎曲模量 [MPa]: 2.20
- 硬度: 106.0
- 熱變形溫度 [℃]: 67.0
- 透光率 [%]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 109 % | 109 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.940 J/cm | 1.76 ft-lb/in | Testing conducted using 10 standard flex bars with 20 mil notch; 9 complete break and 1 nonbreak.; ASTM D256 |
| 0.520 J/cm @Temperature -40.0 °C | 0.974 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ASTM D648 |
| Vicat Softening Point | 79.0 °C | 174 °F | 1 kg load; ASTM D 1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.60 % | 0.60 % | ASTM D1003 |
| Gloss | 171 % | 171 % | at 60°; ASTM D 2457 |
| Transmission, Visible | 88 % | 88 % | Regular transmittance per ASTM D 1003 |
| 90 % | 90 % | Total Transmittance; ASTM D 1003 | |