- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.36
- 拉伸強度 [MPa]: 57.0
- 斷裂伸長率 [%]: 81.0
- 彎曲模量 [MPa]: 2.50
- 硬度: 110.0
- 熱變形溫度 [℃]: 66.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 | ||
| Bulk Density | 0.817 g/cc | 0.0295 lb/in3 | Poured; ASTM D1895 | ||
| 0.881 g/cc | 0.0318 lb/in3 | Vibrated; ASTM D1895 | |||
| Density | 1.40 g/cc | 0.0506 lb/in3 | Crystalline Density; ASTM D1505 | ||
| Melt Density | 1.20 g/cc @Temperature 285 °C | 0.0434 lb/in3 @Temperature 545 °F | ASTM D1238 | ||
| Water Absorption | 0.10 % | 0.10 % | 24h Immersion; ASTM D570 | ||
| Particle Size | 2500 μm | 2500 μm | Pellet Size | ||
| Viscosity Measurement | 0.72 - 0.76 | 0.72 - 0.76 | Intrinsic; VGAS-A-AN-G-V-1 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 110 | 110 | ASTM D785 | ||
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 | ||
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | ASTM D638 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 | ||
| Flexural Yield Strength | 81.0 MPa | 11700 psi | ASTM D790 | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.360 J/cm @Temperature -40.0 °C | 0.674 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 0.510 J/cm @Temperature 23.0 °C | 0.955 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Izod Impact, Unnotched | NB | NB | ASTM D4812 | ||
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D4812 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 | ||
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | ASTM D150 | ||
| 3.2 @Frequency 1000 Hz | 3.2 @Frequency 1000 Hz | ASTM D150 | |||
| Dielectric Strength | 15.7 kV/mm | 399 kV/in | Short Time, 500V/sec; ASTM D149 | ||
| Dissipation Factor | 0.0080 @Frequency 1000 Hz | 0.0080 @Frequency 1000 Hz | ASTM D150 | ||
| 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ASTM D150 | |||
| Arc Resistance | 155 sec | 155 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 63.0 J/g | 27.1 BTU/lb | ASTM E793 | ||
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | ASTM E1269 | ||
| 1.30 J/g-°C @Temperature 80.0 °C | 0.311 BTU/lb-°F @Temperature 176 °F | ASTM E1269 | |||
| 1.40 J/g-°C @Temperature 100 °C | 0.335 BTU/lb-°F @Temperature 212 °F | ASTM E1269 | |||
| 1.90 J/g-°C @Temperature 200 °C | 0.454 BTU/lb-°F @Temperature 392 °F | ASTM E1269 | |||
| 2.10 J/g-°C @Temperature 280 °C | 0.502 BTU/lb-°F @Temperature 536 °F | ASTM E1269 | |||
| Melting Point | 250 °C | 482 °F | Crystalline Peak Melting Point; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ASTM D648 | ||
| Vicat Softening Point | 79.0 °C | 174 °F | 1kg load; ASTM D1525 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 - 295 °C | 527 - 563 °F | |||
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |||
| Drying Temperature | 150 - 160 °C | 302 - 320 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | |||
| Descriptive Properties | |||||
| Acetaldehyde | <3ppm | VKCA-A-AS-G-GC-0001 | |||
| Color, CIE a* | -2.0 ± 1.5 | VGAS-A-AN-G-RS-001 | |||
| Color, CIE b* | 0.4 ± 1.5 | VGAS-A-AN-G-RS-001 | |||
| Color, CIE L* | 78.5 min | VGAS-A-AN-G-RS-001 | |||
| Fines, wt%, max | 0.05 | VGAS-A-AN-G-GA-1 | |||
| Pellet Shape | Cubical | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.