- 熔體流動速率 [g/10min]: 8.5
- 密度 [g/cm3]: 1.23
- 缺口沖擊強度: 7.5
- 拉伸強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 2.10
- 硬度: 111.0
- 熱變形溫度 [℃]: 117.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 8.5 g/10 min @Load 5.00 kg, Temperature 260 °C | 8.5 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 111 @Thickness 3.20 mm | 111 @Thickness 0.126 in | Injection Molded; ASTM D785 |
| Tensile Strength at Break | 56.2 MPa @Thickness 3.20 mm | 8150 psi @Thickness 0.126 in | 50 mm/min, Injection Molded; ASTM D638 |
| Tensile Strength, Yield | 50.0 MPa @Thickness 3.20 mm | 7250 psi @Thickness 0.126 in | 50 mm/min, Injection Molded; ASTM D638 |
| Elongation at Break | 150 % @Thickness 3.20 mm | 150 % @Thickness 0.126 in | 50 mm/min, Injection Molded; ASTM D638 |
| Elongation at Yield | 4.7 % @Thickness 3.20 mm | 4.7 % @Thickness 0.126 in | 50 mm/min, Injection Molded; ASTM D638 |
| Tensile Modulus | 2.21 GPa @Thickness 3.20 mm | 321 ksi @Thickness 0.126 in | 5 mm/min, Injection Molded; ASTM D638 |
| Flexural Strength | 77.2 MPa @Thickness 3.20 mm | 11200 psi @Thickness 0.126 in | 1.3 mm/min, Injection Molded; ASTM D790 |
| Flexural Modulus | 2.10 GPa @Thickness 3.20 mm | 305 ksi @Thickness 0.126 in | 1.3 mm/min, Injection Molded; ASTM D790 |
| Izod Impact, Notched | 7.50 J/cm @Thickness 3.20 mm, Temperature -30.0 °C | 14.1 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F | Injection Molded; ASTM D256 |
| 9.50 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 17.8 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | Injection Molded; ASTM D256 | |
| Dart Drop, Total Energy | 46.3 J @Thickness 3.20 mm, Temperature 23.0 °C | 34.1 ft-lb @Thickness 0.126 in, Temperature 73.4 °F | Injection Molded, Peak Energy; ASTM D3763 |
| 55.4 J @Thickness 3.20 mm, Temperature -40.0 °C | 40.9 ft-lb @Thickness 0.126 in, Temperature -40.0 °F | Injection Molded, Peak Energy; ASTM D3763 | |
| 63.3 J @Thickness 3.20 mm, Temperature 23.0 °C | 46.7 ft-lb @Thickness 0.126 in, Temperature 73.4 °F | Injection Molded, Total Energy; ASTM D3763 | |
| 80.2 J @Thickness 3.20 mm, Temperature -40.0 °C | 59.2 ft-lb @Thickness 0.126 in, Temperature -40.0 °F | Injection Molded, Total Energy; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C | 243 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C | 189 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 144 °C @Load 1.02 kg | 291 °F @Load 2.25 lb | Rate B (120°C/h); ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 249 - 282 °C | 480 - 540 °F | |
| Mold Temperature | 43.3 - 65.6 °C | 110 - 150 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | |