- 成型收縮率 [%]: 0.003
- 缺口沖擊強度: 0.59
- 彎曲模量 [MPa]: 9.60
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.20 mm | 0.0030 in/in @Thickness 0.126 in | Flow | ||
| 0.0090 cm/cm @Thickness 3.20 mm | 0.0090 in/in @Thickness 0.126 in | Transverse | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 94.0 MPa @Temperature 23.0 °C | 13600 psi @Temperature 73.4 °F | ISO 527 | ||
| Tensile Strength | 94.0 MPa @Temperature 23.0 °C | 13600 psi @Temperature 73.4 °F | ASTM D638 | ||
| Elongation at Break | 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | ISO 527 | ||
| 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | ASTM D638 | |||
| Flexural Strength | 147 MPa @Temperature 23.0 °C | 21300 psi @Temperature 73.4 °F | ASTM D790 | ||
| Flexural Modulus | 9.60 GPa @Temperature 23.0 °C | 1390 ksi @Temperature 73.4 °F | ASTM D790 | ||
| Izod Impact, Notched | 0.590 J/cm @Temperature 23.0 °C | 1.11 ft-lb/in @Temperature 73.4 °F | ASTM D256 | ||
| Izod Impact, Unnotched | 5.00 J/cm @Temperature 23.0 °C | 9.37 ft-lb/in @Temperature 73.4 °F | ASTM D4812 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.8 kV/mm @Thickness 3.20 mm, Temperature 200 °C | 351 kV/in @Thickness 0.126 in, Temperature 392 °F | Short Time; ASTM D149 | ||
| 25.6 kV/mm @Thickness 3.20 mm, Temperature 120 °C | 650 kV/in @Thickness 0.126 in, Temperature 248 °F | Short Time; ASTM D149 | |||
| >= 28.0 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | >= 711 kV/in @Thickness 0.126 in, Temperature 73.4 °F | Short Time; ASTM D149 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | ISO 75-1/-2 | ||
| 216 °C | 421 °F | ASTM D648 | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | UL94 | ||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | >= 95.0 °C | >= 203 °F | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | ||||
| Features | Dimensional Stability, Good | ||||
| Electrical Properties, Good | |||||
| Stiffness, Good | |||||
| Strength, Good | |||||
| Thermal Aging Resistance, Good | |||||
| Warp Resistant | |||||
| Filler | Glass/Mica | ||||
| Forms | Pellets | ||||
| Generic | PET | ||||
| Heat Stabilized | Yes | ||||
| Material Status | Current | ||||
| Part Marking Code | >PET-(GF+MD)35< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PET | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Glass/Mineral Reinforced Resins | |||||
| Low Warp Resins | |||||
| Resin Identification | PET-(GF+MD)35 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Ultrasonic Weldable | Yes | ||||
| Uses | Automotive Applications | ||||
| Electrical Parts | |||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Phenolic Replacement | |||||
| Structural Parts | |||||