- 吸水率 [%]: 0.1
- 缺口沖擊強度: 7.0
- 彎曲模量 [MPa]: 2.30
- 硬度: 95.0
- 熱變形溫度 [℃]: 110.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.24 g/cc @Temperature 23.0 °C | 1.24 g/cc @Temperature 73.4 °F | ASTM D792 | ||
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec | 0.10 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm @Temperature 23.0 °C | 0.0040 - 0.0070 in/in @Temperature 73.4 °F | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 95 | 95 | ASTM D785 | ||
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 100 % | 100 % | 50mm/min; ASTM D638 | ||
| Flexural Strength | 85.0 MPa | 12300 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 2.30 GPa | 334 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | >= 7.00 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | >= 13.1 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | ||
| Izod Impact, Unnotched | NB @Thickness 3.20 mm, Temperature 23.0 °C | NB @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ASTM D257 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | 1.6mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 6.40 mm | 230 °F @Thickness 0.252 in | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm | 212 °F @Thickness 0.252 in | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 280 °C | <= 536 °F | |||
| Rear Barrel Temperature | 245 - 260 °C | 473 - 500 °F | Start Point: 250°C | ||
| Middle Barrel Temperature | 250 - 270 °C | 482 - 518 °F | Start Point: 255°C | ||
| Front Barrel Temperature | 250 - 270 °C | 482 - 518 °F | Start Point: 260°C | ||
| Melt Temperature | 245 - 270 °C | 473 - 518 °F | Start Point: 260°C | ||
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Start Point: 80°C | ||
| Drying Temperature | 120 °C @Time 14400 - 21600 sec | 248 °F @Time 4.00 - 6.00 hour | Pre-dry | ||
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |||
| Descriptive Properties | |||||
| Injection Speed | 60-100% | ||||