- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 5.2
- 熱變形溫度 [℃]: 230.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | ISO 1183 |
| Water Absorption at Saturation | 5.2 % | 5.2 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 89 | 89 | ISO 868 |
| Ball Indentation Hardness | 250 MPa | 36300 psi | H30; ISO 2039-1 |
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527-1/2 |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527-1/2 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 6.00 J/cm2 @Temperature -30.0 °C | 28.6 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 6.50 J/cm2 @Temperature 23.0 °C | 30.9 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.950 J/cm2 @Temperature -30.0 °C | 4.52 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 1.00 J/cm2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 11.1 μin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359, DIN 53752 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 230 °C | >= 446 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 230 °C | >= 446 °F | ISO 75-1/-2 |
| Vicat Softening Point | >= 230 °C | >= 446 °F | Method A, 10 N; ISO 306 |
| >= 230 °C | >= 446 °F | Method B, 50 N; ISO 306 | |