- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.31
- 拉伸強度 [MPa]: 30.0
- 熱變形溫度 [℃]: 140.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | |
| Water Absorption | 0.00 % | 0.00 % | |
| Melt Flow | 12 g/10 min | 12 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 14 % | 14 % | |
| Modulus of Elasticity | 0.750 GPa | 109 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 9.00 J/cm2 @Temperature -30.0 °C | 42.8 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.900 J/cm2 | 4.28 ft-lb/in2 | |
| 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | |
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | <= 50.0 μm/m-°C @Temperature 20.0 °C | <= 27.8 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |
| Vicat Softening Point | 190 °C | 374 °F | 50°C/hr/50 N |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||