- 密度 [g/cm3]: 1.389
- 缺口沖擊強度: 4.4
- 彎曲模量 [MPa]: 4.852
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.389 g/cc | 0.05018 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Break | 3.0 % | 3.0 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 5.176 GPa | 750.7 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 133 MPa | 19300 psi | ISO 178 |
| Flexural Modulus | 4.852 GPa | 703.7 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.40 kJ/m2 | 2.09 ft-lb/in2 | ISO 180/1A |
| Charpy Impact Unnotched | 2.00 J/cm2 | 9.52 ft-lb/in2 | ISO 179/1eU |
| 1.80 J/cm2 @Temperature 30.0 °C | 8.57 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.510 J/cm2 | 2.43 ft-lb/in2 | ISO 179/1eA |
| 0.490 J/cm2 @Temperature 30.0 °C | 2.33 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper |
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |