- 熔體流動速率 [g/10min]: 65.0
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.09
- 缺口沖擊強度: 0.374
- 拉伸強度 [MPa]: 60.0
- 彎曲模量 [MPa]: 2.60
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 | ||
| Density | 1.31 g/cc | 0.0473 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.090 % @Temperature 22.8 °C | 0.090 % @Temperature 73.0 °F | 24hr immersion; ASTM D570 | ||
| Viscosity Test | 75 cm3/g | 75 cm3/g | ISO 307, 1157, 1628 | ||
| Linear Mold Shrinkage, Flow | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | ASTM D955 | ||
| 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | ISO 294-4 | |||
| Melt Flow | 65 g/10 min | 65 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 75 | 75 | ISO 2039-2 | ||
| Tensile Stress | 8.62 MPa @Strain 0.320 %, Temperature 23.0 °C | 1250 psi @Strain 0.320 %, Temperature 73.4 °F | |||
| 16.8 MPa @Strain 0.640 %, Temperature 23.0 °C | 2440 psi @Strain 0.640 %, Temperature 73.4 °F | ||||
| 24.6 MPa @Strain 0.960 %, Temperature 23.0 °C | 3570 psi @Strain 0.960 %, Temperature 73.4 °F | ||||
| 31.8 MPa @Strain 1.28 %, Temperature 23.0 °C | 4610 psi @Strain 1.28 %, Temperature 73.4 °F | ||||
| 38.2 MPa @Strain 1.60 %, Temperature 23.0 °C | 5540 psi @Strain 1.60 %, Temperature 73.4 °F | ||||
| 43.6 MPa @Strain 1.92 %, Temperature 23.0 °C | 6320 psi @Strain 1.92 %, Temperature 73.4 °F | ||||
| 47.6 MPa @Strain 2.24 %, Temperature 23.0 °C | 6900 psi @Strain 2.24 %, Temperature 73.4 °F | ||||
| 49.8 MPa @Strain 2.56 %, Temperature 23.0 °C | 7220 psi @Strain 2.56 %, Temperature 73.4 °F | ||||
| 50.8 MPa @Strain 2.88 %, Temperature 23.0 °C | 7370 psi @Strain 2.88 %, Temperature 73.4 °F | ||||
| 51.1 MPa @Strain 3.20 %, Temperature 23.0 °C | 7410 psi @Strain 3.20 %, Temperature 73.4 °F | ||||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ISO 527-2/1A | ||
| 57.2 MPa @Temperature 22.8 °C | 8300 psi @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Break | 30 % | 30 % | 50mm/min; ISO 527-2/1A | ||
| 5.0 % @Temperature 22.8 °C | 5.0 % @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.70 GPa | 392 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 | ||
| 85.5 MPa @Temperature 22.8 °C | 12400 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178 | ||
| 2.48 GPa @Temperature 22.8 °C | 360 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Shear Modulus | 0.0181 GPa @Temperature 220 °C | 2.63 ksi @Temperature 428 °F | |||
| 0.0380 GPa @Temperature 210 °C | 5.51 ksi @Temperature 410 °F | ||||
| 0.0481 GPa @Temperature 200 °C | 6.98 ksi @Temperature 392 °F | ||||
| 0.0552 GPa @Temperature 190 °C | 8.01 ksi @Temperature 374 °F | ||||
| 0.0623 GPa @Temperature 180 °C | 9.04 ksi @Temperature 356 °F | ||||
| 0.0682 GPa @Temperature 170 °C | 9.89 ksi @Temperature 338 °F | ||||
| 0.0739 GPa @Temperature 160 °C | 10.7 ksi @Temperature 320 °F | ||||
| 0.0796 GPa @Temperature 150 °C | 11.5 ksi @Temperature 302 °F | ||||
| 0.0861 GPa @Temperature 140 °C | 12.5 ksi @Temperature 284 °F | ||||
| 0.0935 GPa @Temperature 130 °C | 13.6 ksi @Temperature 266 °F | ||||
| 0.101 GPa @Temperature 120 °C | 14.6 ksi @Temperature 248 °F | ||||
| 0.111 GPa @Temperature 110 °C | 16.1 ksi @Temperature 230 °F | ||||
| 0.122 GPa @Temperature 100 °C | 17.7 ksi @Temperature 212 °F | ||||
| 0.139 GPa @Temperature 90.0 °C | 20.2 ksi @Temperature 194 °F | ||||
| 0.168 GPa @Temperature 80.0 °C | 24.4 ksi @Temperature 176 °F | ||||
| 0.220 GPa @Temperature 70.0 °C | 31.9 ksi @Temperature 158 °F | ||||
| 0.334 GPa @Temperature 60.0 °C | 48.4 ksi @Temperature 140 °F | ||||
| 0.572 GPa @Temperature 50.0 °C | 83.0 ksi @Temperature 122 °F | ||||
| 0.734 GPa @Temperature 40.0 °C | 106 ksi @Temperature 104 °F | ||||
| 0.773 GPa @Temperature 30.0 °C | 112 ksi @Temperature 86.0 °F | ||||
| 0.797 GPa @Temperature 23.0 °C | 116 ksi @Temperature 73.4 °F | ||||
| 0.832 GPa @Temperature 10.0 °C | 121 ksi @Temperature 50.0 °F | ||||
| 0.855 GPa @Temperature 0.000 °C | 124 ksi @Temperature 32.0 °F | ||||
| 0.879 GPa @Temperature -10.0 °C | 127 ksi @Temperature 14.0 °F | ||||
| 0.904 GPa @Temperature -20.0 °C | 131 ksi @Temperature -4.00 °F | ||||
| 0.930 GPa @Temperature -30.0 °C | 135 ksi @Temperature -22.0 °F | ||||
| 0.961 GPa @Temperature -40.0 °C | 139 ksi @Temperature -40.0 °F | ||||
| 0.986 GPa @Temperature -50.0 °C | 143 ksi @Temperature -58.0 °F | ||||
| 1.07 GPa @Temperature -60.0 °C | 155 ksi @Temperature -76.0 °F | ||||
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C | 0.700 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 3.20 kJ/m2 | 1.52 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact Unnotched | 10.0 J/cm2 | 47.6 ft-lb/in2 | ISO 179/1eU | ||
| 9.00 J/cm2 @Temperature 30.0 °C | 42.8 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179/1eA | ||
| 0.350 J/cm2 @Temperature 30.0 °C | 1.67 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | short term; ASTM D149 | ||
| 23.0 kV/mm | 584 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.0015 @Frequency 100 Hz | 0.0015 @Frequency 100 Hz | IEC 60250 | ||
| 0.0020 @Frequency 1.00e+6 Hz | 0.0020 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 μm/m-°C | 61.1 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 86.0 μm/m-°C | 47.8 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ISO 75-1, -2 | ||
| 162 °C | 324 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.6 °C | 123 °F | ASTM D648 | ||
| 55.0 °C | 131 °F | ISO 75-1, -2 | |||
| Vicat Softening Point | 190 °C | 374 °F | B50 (50°C/h 50N); ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |||
| Oxygen Index | 22 % | 22 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 243 °C | 469 °F | ISO 294 | ||
| 235 - 260 °C | 455 - 500 °F | ||||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Processing conditions acc. ISO | 7792-2 | ||||