- 熔體流動速率 [g/10min]: 23.0
- 密度 [g/cm3]: 1.45
- 缺口沖擊強度: 0.737
- 彎曲模量 [MPa]: 6.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 | ||
| Density | 1.45 g/cc | 0.0524 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 | ||
| 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ISO 294-4 | |||
| Melt Flow | 23 g/10 min | 23 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | 5mm/min; ISO 527-2/1A | ||
| 115 MPa @Temperature 22.8 °C | 16700 psi @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Break | 3.2 % | 3.2 % | 5mm/min; ISO 527-2/1A | ||
| 2.8 % @Temperature 22.8 °C | 2.8 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 7.03 GPa @Temperature 22.8 °C | 1020 ksi @Temperature 73.0 °F | ASTM D638 | ||
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 | ||
| 175.6 MPa @Temperature 22.8 °C | 25470 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 | ||
| 6.83 GPa @Temperature 22.8 °C | 990 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.737 J/cm @Temperature 22.8 °C | 1.38 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | ISO 180/1A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 107 °C | 225 °F | ASTM D3418 | ||
| 225 °C | 437 °F | ISO 11357-1,-2,-3 | |||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection speed | medium-fast | ||||