- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 1.6
- 拉伸強度 [MPa]: 44.1
- 彎曲模量 [MPa]: 1.90
- 熱變形溫度 [℃]: 128.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Density | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.100 % | 0.100 % | 24hr immersion; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0130 - 0.0150 cm/cm | 0.0130 - 0.0150 in/in | ASTM D955 | ||
| 0.0130 - 0.0150 cm/cm | 0.0130 - 0.0150 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0130 - 0.0150 cm/cm | 0.0130 - 0.0150 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 104 | 104 | ISO 2039-2 | ||
| Tensile Stress | 30.0 MPa @Strain 50.0 % | 4350 psi @Strain 50.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM D638 | ||
| Elongation at Break | >= 50.0 % | >= 50.0 % | 50mm/min; ISO 527-2/1A | ||
| 80.0 % @Temperature 22.8 °C | 80.0 % @Temperature 73.0 °F | ASTM D638 | |||
| Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 | ||
| 63.4 MPa | 9200 psi | ASTM D790 | |||
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 | ||
| 2.24 GPa @Temperature 22.8 °C | 325 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 | ||
| 0.534 J/cm @Temperature -28.9 °C | 1.00 ft-lb/in @Temperature -20.0 °F | ASTM D256 | |||
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | ISO 180/1A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | ISO 75-1, -2 | ||
| 132 °C | 270 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 | ||
| 53.0 °C | 127 °F | ISO 75-1, -2 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 240 - 265 °C | 464 - 509 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 240 - 265 °C | 464 - 509 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 86.0 MPa | 12500 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Screw Speed - Moderate | |||||