- 密度 [g/cm3]: 1.21
- 缺口沖擊強度: 6.9
- 拉伸強度 [MPa]: 60.0
- 斷裂伸長率 [%]: 90.0
- 彎曲模量 [MPa]: 2.40
- 熱變形溫度 [℃]: 113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 6.90 J/cm | 12.9 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |