- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.75
- 拉伸強度 [MPa]: 130.0
- 彎曲模量 [MPa]: 8.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in3 | ASTM D792, ISO 1183 |
| Water Absorption | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | 24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0025 - 0.015 cm/cm | 0.0025 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638, ISO R527 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638, ISO R527 |
| Flexural Strength | 190 MPa | 27600 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.750 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.41 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256, ISO 180/4a |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.8 @Frequency 1000 Hz | 3.8 @Frequency 1000 Hz | ASTM D150, IEC 250 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz | 0.0020 @Frequency 1000 Hz | ASTM D150, IEC 250 |
| Comparative Tracking Index | 400 V | 400 V | VDE 0303-P1, IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 140 °C | 284 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 160 °C | 320 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 200 °C | 392 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 210 °C @Load 5.00 kg | 410 °F @Load 11.0 lb | 120°C/min; ASTM D1525/B, ISO 306/B |
| 220 °C @Load 0.999 kg | 428 °F @Load 2.20 lb | 120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||