- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.25
- 缺口沖擊強度: 6.41
- 拉伸強度 [MPa]: 46.9
- 斷裂伸長率 [%]: 72.4
- 彎曲模量 [MPa]: 2.07
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | ASTM D792 | ||
| Melt Flow | 20 g/10 min @Load 3.80 kg, Temperature 250 °C | 20 g/10 min @Load 8.38 lb, Temperature 482 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 46.9 MPa | 6800 psi | ASTM D638 | ||
| Flexural Yield Strength | 72.4 MPa | 10500 psi | ASTM D790 | ||
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 | ||
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | 73°F, 0.125 in; ASTM D256 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 243 - 266 °C | 470 - 510 °F | |||
| Middle Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |||
| Front Barrel Temperature | 254 - 277 °C | 490 - 530 °F | |||
| Nozzle Temperature | 254 - 271 °C | 490 - 520 °F | |||
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | |||
| Shot Size | 50 - 80 % | 50 - 80 % | |||
| Screw Speed | 50 - 80 rpm | 50 - 80 rpm | |||
| Descriptive Properties | |||||
| Injection Rate | Moderate | ||||