- 熔體流動速率 [g/10min]: 43.5
- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.4
- 拉伸強度 [MPa]: 65.0
- 熱變形溫度 [℃]: 170.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C; 50% RH | ||
| Viscosity Measurement | 123 | 123 | [ml/g]; Viscosity number; ISO 1628 | ||
| 70 @Temperature 290 °C | 70 @Temperature 554 °F | 20 mins plasticating | |||
| 75 @Temperature 300 °C | 75 @Temperature 572 °F | 10 mins plasticating | |||
| 75 @Temperature 280 °C | 75 @Temperature 536 °F | 30 mins plasticating | |||
| 90 @Temperature 270 °C | 90 @Temperature 518 °F | 30 mins plasticating | |||
| 95 @Temperature 290 °C | 95 @Temperature 554 °F | 10 mins plasticating | |||
| 100 @Temperature 260 °C | 100 @Temperature 500 °F | 30 mins plasticating | |||
| 100 @Temperature 300 °C | 100 @Temperature 572 °F | 5 mins plasticating | |||
| 105 @Temperature 280 °C | 105 @Temperature 536 °F | 10 mins plasticating | |||
| 106 @Temperature 250 °C | 106 @Temperature 482 °F | 30 mins plasticating | |||
| 110 @Temperature 270 °C | 110 @Temperature 518 °F | 10 mins plasticating | |||
| 115 @Temperature 260 °C | 115 @Temperature 500 °F | 10 mins plasticating | |||
| 115 @Temperature 240 °C | 115 @Temperature 464 °F | 30 mins plasticating | |||
| 117 @Temperature 250 °C | 117 @Temperature 482 °F | 10 mins plasticating | |||
| 120 @Temperature 240 °C | 120 @Temperature 464 °F | 10 mins plasticating | |||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | Sheet | ||
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | Sheet | ||
| Melt Flow | 43.5 g/10 min @Load 2.16 kg, Temperature 250 °C | 43.5 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 120 MPa | 17400 psi | ISO 2039-1 | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 5.3 % | 5.3 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.9 % | 3.9 % | 50 mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 5.00 J/cm2 | 23.8 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179/1eA | ||
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | W501 housing; ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 1300 MPa @Strain <=0.500 % | 189000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 93 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 93 | ||
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 250 | ||
| 3.3 @Frequency 100 Hz | 3.3 @Frequency 100 Hz | IEC 250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.011 @Frequency 100 Hz | 0.011 @Frequency 100 Hz | IEC 250 | ||
| 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 250 | |||
| Comparative Tracking Index | 150 V | 150 V | Test solution B; IEC 112 | ||
| 250 V | 250 V | Test solution A; IEC 112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.500 - 0.600 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.278 - 0.333 μin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | IEC 1006 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 135 °C | 275 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-2 | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||||
| V-0 @Diameter 0.400 mm | V-0 @Diameter 0.0157 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 240 °C | 464 °F | Feeding zone | ||
| Zone 2 | 245 °C | 473 °F | Compression | ||
| Zone 3 | 250 °C | 482 °F | Metering-zone | ||
| Zone 4 | 250 °C | 482 °F | Nozzle | ||
| Melt Temperature | 250 °C | 482 °F | Optimal | ||
| 260 °C | 500 °F | for shrinkage test | |||
| 245 - 275 °C | 473 - 527 °F | Injection-molding | |||
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | |||
| 60.0 °C | 140 °F | for shrinkage test, Optimal | |||
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Descriptive Properties | |||||
| Color | Natural, Colored, Black and Special Colors | ||||
| Commercial Status | Europe | ||||
| Peripheral Screw Speed | <0.25 m/s | ||||
| Primary Processing Technique | Injection Molding | ||||