- 熔體流動速率 [g/10min]: 14.19
- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 0.4
- 拉伸強(qiáng)度 [MPa]: 63.0
- 熱變形溫度 [℃]: 195.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 139 | 139 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | Sheet | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | Sheet | ||
| Melt Flow | 14.19 g/10 min @Load 2.16 kg, Temperature 275 °C | 14.19 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 3.8 % | 3.8 % | 50mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 4.00 GPa | 580 ksi | ISO 527-2 | ||
| Flexural Strength | 104 MPa | 15100 psi | ISO 178 | ||
| Charpy Impact Unnotched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.450 J/cm2 | 2.14 ft-lb/in2 | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Maximum Service Temperature, Air | 170 °C | 338 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Europe | ||||
| Primary Processing Technique | Injection Molding | ||||