- 熔體流動速率 [g/10min]: 50.0
- 密度 [g/cm3]: 1.56
- 彎曲強度 [MPa]: 135.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | ISO 1183 | ||
| Viscosity Test | 87 cm3/g | 87 cm3/g | Viscosity number | ||
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 275 °C | 50 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 1.8 % | 1.8 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 10.7 GPa | 1550 ksi | 1mm/min; ISO 527 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 232 °C | 450 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK15029 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||