- 熔體流動速率 [g/10min]: 53.0
- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 0.4
- 拉伸強度 [MPa]: 140.0
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 80 cm3/g | 80 cm3/g | Viscosity number | ||
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm | 0.0029 in/in | ISO 294 | ||
| Linear Mold Shrinkage, Transverse | 0.0097 cm/cm | 0.0097 in/in | ISO 294 | ||
| Melt Flow | 53.0 g/10 min @Load 2.16 kg, Temperature 275 °C | 53.0 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 140 MPa | 20300 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 2.1 % | 2.1 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 10.5 GPa | 1520 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 4.80 J/cm2 | 22.8 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.750 J/cm2 | 3.57 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 225 V | 225 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | |||
| Maximum Service Temperature, Air | 210 °C | 410 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 40.6 mm | HB @Thickness 1.60 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Descriptive Properties | |||||
| Color | BK15029 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||