- 缺口沖擊強度: 1.51
- 彎曲模量 [MPa]: 8.06269
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.175 mm | 0.0020 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 117.39 MPa | 17026 psi | ASTM D638 |
| Flexural Strength | 181.5 MPa | 26320 psi | ASTM D790 |
| Flexural Modulus | 8.06269 GPa | 1169.39 ksi | ASTM D790 |
| Izod Impact, Notched | 1.51 J/cm | 2.82 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 252 - 260 °C | 485 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |