- 密度 [g/cm3]: 1.63
- 缺口沖擊強度: 0.59
- 彎曲強度 [MPa]: 101.0
- 彎曲模量 [MPa]: 8.70
- 硬度: 119.0
- 熱變形溫度 [℃]: 202.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in3 | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 101 MPa | 14600 psi | ASTM D638 |
| Elongation at Break | 6.6 % | 6.6 % | ASTM D638 |
| Flexural Strength | 149 MPa | 21600 psi | ASTM D790 |
| Flexural Modulus | 8.70 GPa | 1260 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.86 J/cm | 9.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 258 - 268 °C | 496 - 514 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 235 - 249 °C | 455 - 480 °F | Approximate middle barrel temperature range |