- 密度 [g/cm3]: 1.7
- 缺口沖擊強度: 0.8
- 彎曲強度 [MPa]: 125.0
- 彎曲模量 [MPa]: 11.0
- 硬度: 117.0
- 熱變形溫度 [℃]: 248.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in3 | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| Flexural Strength | 191 MPa | 27700 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.95 J/cm | 7.40 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 248 °C | 478 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 235 - 249 °C | 455 - 480 °F | Approximate middle barrel temperature range |