- 密度 [g/cm3]: 1.54
- 缺口沖擊強度: 0.91
- 彎曲強度 [MPa]: 99.0
- 彎曲模量 [MPa]: 9.60
- 硬度: 115.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in3 | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 99.0 MPa | 14400 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 161 MPa | 23400 psi | ASTM D790 |
| Flexural Modulus | 9.60 GPa | 1390 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 240 °C | 464 °F | Approximate middle barrel temperature. |