- 密度 [g/cm3]: 1.26
- 缺口沖擊強度: 8.11
- 彎曲強度 [MPa]: 28.0
- 彎曲模量 [MPa]: 1.70
- 硬度: 107.0
- 熱變形溫度 [℃]: 154.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in3 | |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 34.2 % | 34.2 % | ASTM D638 |
| Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ASTM D790 |
| Izod Impact, Notched | 8.11 J/cm | 15.2 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 224 - 241 °C | 435 - 466 °F | Approximate middle barrel temperature range |