- 熔體流動速率 [g/10min]: 1.9
- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 0.03
- 缺口沖擊強(qiáng)度: 0.35
- 拉伸強(qiáng)度 [MPa]: 33.0
- 斷裂伸長率 [%]: 43.0
- 彎曲強(qiáng)度 [MPa]: 31.0
- 彎曲模量 [MPa]: 1.55
- 硬度: 95.0
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 - 1.60 g/cc | 0.0397 - 0.0578 lb/in3 | Average value: 1.24 g/cc Grade Count:257 |
| 1.02 - 1.03 g/cc @Temperature 260 - 260 °C | 0.0368 - 0.0372 lb/in3 @Temperature 500 - 500 °F | Average value: 1.02 g/cc Grade Count:15 | |
| Water Absorption | 0.0300 - 0.500 % | 0.0300 - 0.500 % | Average value: 0.200 % Grade Count:61 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.122 % Grade Count:101 |
| Water Absorption at Saturation | 0.0100 - 0.500 % | 0.0100 - 0.500 % | Average value: 0.337 % Grade Count:84 |
| Viscosity | 100000 - 295000 cP | 100000 - 295000 cP | Average value: 235000 cP Grade Count:11 |
| Maximum Moisture Content | 0.0200 | 0.0200 | Average value: 0.0200 Grade Count:18 |
| Linear Mold Shrinkage | 0.0000300 - 0.0200 cm/cm | 0.0000300 - 0.0200 in/in | Average value: 0.00868 cm/cm Grade Count:214 |
| Linear Mold Shrinkage, Transverse | 0.00110 - 0.0180 cm/cm | 0.00110 - 0.0180 in/in | Average value: 0.00910 cm/cm Grade Count:48 |
| Melt Flow | 1.90 - 60.0 g/10 min | 1.90 - 60.0 g/10 min | Average value: 14.6 g/10 min Grade Count:166 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 80.0 - 89.0 | 80.0 - 89.0 | Average value: 86.8 Grade Count:4 |
| Hardness, Rockwell R | 95.0 - 119 | 95.0 - 119 | Average value: 114 Grade Count:30 |
| Hardness, H358/30 | 81.0 - 114 MPa | 11700 - 16500 psi | Average value: 97.2 MPa Grade Count:29 |
| Hardness, Shore D | 76.0 - 79.0 | 76.0 - 79.0 | Average value: 76.6 Grade Count:5 |
| Tensile Strength, Ultimate | 31.0 - 110 MPa | 4500 - 16000 psi | Average value: 51.2 MPa Grade Count:133 |
| Tensile Strength, Yield | 33.0 - 142 MPa | 4790 - 20600 psi | Average value: 53.6 MPa Grade Count:223 |
| Elongation at Break | 2.00 - 250 % | 2.00 - 250 % | Average value: 97.5 % Grade Count:214 |
| Elongation at Yield | 2.00 - 20.0 % | 2.00 - 20.0 % | Average value: 4.57 % Grade Count:134 |
| Modulus of Elasticity | 1.40 - 5.12 GPa | 203 - 743 ksi | Average value: 2.34 GPa Grade Count:137 |
| Flexural Yield Strength | 43.0 - 192 MPa | 6240 - 27800 psi | Average value: 84.2 MPa Grade Count:214 |
| Flexural Modulus | 1.55 - 19.3 GPa | 225 - 2800 ksi | Average value: 2.47 GPa Grade Count:218 |
| Izod Impact, Notched | 0.350 - 981 J/cm | 0.656 - 1840 ft-lb/in | Average value: 6.77 J/cm Grade Count:196 |
| 0.300 - 7.50 J/cm @Temperature -50.0 - 0.000 °C | 0.562 - 14.1 ft-lb/in @Temperature -58.0 - 32.0 °F | Average value: 3.72 J/cm Grade Count:92 | |
| 1.00 - 7.84532 J/cm @Temperature -40.0 - -20.0 °C | 1.87 - 14.6975 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 3.72 J/cm Grade Count:35 | |
| 1.00 - 7.84532 J/cm @Thickness 1.57 - 6.40 mm | 1.87 - 14.6975 ft-lb/in @Thickness 0.0618 - 0.252 in | Average value: 3.72 J/cm Grade Count:35 | |
| Izod Impact, Unnotched | 4.30 J/cm - NB | 8.06 ft-lb/in - NB | Average value: 12.0 J/cm Grade Count:32 |
| 3.20 J/cm - NB @Temperature -30.0 - -30.0 °C | 5.99 ft-lb/in - NB @Temperature -22.0 - -22.0 °F | Average value: 4.07 J/cm Grade Count:13 | |
| 4.50 - 4.50 J/cm @Temperature -40.0 - -40.0 °C | 8.43 - 8.43 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 4.07 J/cm Grade Count:1 | |
| 4.50 - 4.50 J/cm @Thickness 3.20 - 3.20 mm | 8.43 - 8.43 ft-lb/in @Thickness 0.126 - 0.126 in | Average value: 4.07 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 4.00 - 65.0 kJ/m2 | 1.90 - 30.9 ft-lb/in2 | Average value: 45.1 kJ/m2 Grade Count:94 |
| 3.00 - 65.0 kJ/m2 @Temperature -40.0 - 0.000 °C | 1.43 - 30.9 ft-lb/in2 @Temperature -40.0 - 32.0 °F | Average value: 27.2 kJ/m2 Grade Count:99 | |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m2 - NB | 14.8 ft-lb/in2 - NB | Average value: 32.7 kJ/m2 Grade Count:30 |
| 20.0 kJ/m2 - NB @Temperature -40.0 - -30.0 °C | 9.52 ft-lb/in2 - NB @Temperature -40.0 - -22.0 °F | Average value: 20.0 kJ/m2 Grade Count:34 | |
| Charpy Impact Unnotched | 3.30 J/cm2 - NB | 15.7 ft-lb/in2 - NB | Average value: 3.65 J/cm2 Grade Count:51 |
| 2.20 J/cm2 - NB @Temperature -30.0 - -20.0 °C | 10.5 ft-lb/in2 - NB @Temperature -22.0 - -4.00 °F | Average value: 2.85 J/cm2 Grade Count:55 | |
| Charpy Impact, Notched | 0.400 - 7.50 J/cm2 | 1.90 - 35.7 ft-lb/in2 | Average value: 4.79 J/cm2 Grade Count:109 |
| 0.400 - 5.50 J/cm2 @Temperature -30.0 - -20.0 °C | 1.90 - 26.2 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 2.45 J/cm2 Grade Count:63 | |
| Gardner Impact | 43.0 - 54.0 J | 31.7 - 39.8 ft-lb | Average value: 48.5 J Grade Count:5 |
| Dart Drop, Total Energy | 5.11 - 100 J | 3.77 - 73.8 ft-lb | Average value: 52.6 J Grade Count:73 |
| 4.86739 - 70.0 J @Temperature -40.0 - -20.0 °C | 3.59000 - 51.6 ft-lb @Temperature -40.0 - -4.00 °F | Average value: 51.3 J Grade Count:19 | |
| Puncture Energy | 45.0 - 47.0 J | 33.2 - 34.7 ft-lb | Average value: 46.3 J Grade Count:8 |
| 55.0 - 58.0 J @Temperature -30.0 - -30.0 °C | 40.6 - 42.8 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 57.0 J Grade Count:8 | |
| Taber Abrasion, mg/1000 Cycles | 20.0 - 40.0 | 20.0 - 40.0 | Average value: 31.0 Grade Count:25 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 1.00e+17 ohm-cm | 1.00e+13 - 1.00e+17 ohm-cm | Average value: 1.46e+16 ohm-cm Grade Count:69 |
| Surface Resistance | 1.00e+12 - 6.02e+16 ohm | 1.00e+12 - 6.02e+16 ohm | Average value: 3.01e+15 ohm Grade Count:48 |
| Dielectric Constant | 2.80 - 3.80 | 2.80 - 3.80 | Average value: 3.22 Grade Count:55 |
| Dielectric Strength | 14.0 - 35.0 kV/mm | 356 - 889 kV/in | Average value: 22.4 kV/mm Grade Count:54 |
| Dissipation Factor | 0.000600 - 0.0300 | 0.000600 - 0.0300 | Average value: 0.00921 Grade Count:52 |
| Arc Resistance | 0.000 - 180 sec | 0.000 - 180 sec | Average value: 108 sec Grade Count:34 |
| Comparative Tracking Index | 100 - 600 V | 100 - 600 V | Average value: 403 V Grade Count:58 |
| Hot Wire Ignition, HWI | 15.0 - 120 sec | 15.0 - 120 sec | Average value: 54.0 sec Grade Count:28 |
| High Amp Arc Ignition, HAI | 15.0 - 120 arcs | 15.0 - 120 arcs | Average value: 66.5 arcs Grade Count:28 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 150 mm/min | 0.000 - 5.91 in/min | Average value: 92.7 mm/min Grade Count:28 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 21.6 - 171 μm/m-°C | 12.0 - 95.0 μin/in-°F | Average value: 81.3 μm/m-°C Grade Count:139 |
| 16.2 - 124 μm/m-°C @Temperature 60.0 - 138 °C | 9.00 - 68.9 μin/in-°F @Temperature 140 - 280 °F | Average value: 57.4 μm/m-°C Grade Count:10 | |
| CTE, linear, Transverse to Flow | 63.0 - 200 μm/m-°C | 35.0 - 111 μin/in-°F | Average value: 92.3 μm/m-°C Grade Count:106 |
| Specific Heat Capacity | 1.78 - 1.88 J/g-°C | 0.425 - 0.449 BTU/lb-°F | Average value: 1.82 J/g-°C Grade Count:15 |
| Thermal Conductivity | 0.167 - 0.200 W/m-K | 1.16 - 1.39 BTU-in/hr-ft2-°F | Average value: 0.186 W/m-K Grade Count:41 |
| Melting Point | 219 - 271 °C | 426 - 520 °F | Average value: 225 °C Grade Count:15 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 - 215 °C | 176 - 419 °F | Average value: 117 °C Grade Count:177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 216 °C | 122 - 421 °F | Average value: 91.1 °C Grade Count:231 |
| Vicat Softening Point | 100 - 210 °C | 212 - 410 °F | Average value: 129 °C Grade Count:119 |
| UL RTI, Electrical | 75.0 - 125 °C | 167 - 257 °F | Average value: 105 °C Grade Count:37 |
| UL RTI, Mechanical with Impact | 75.0 - 120 °C | 167 - 248 °F | Average value: 103 °C Grade Count:37 |
| UL RTI, Mechanical without Impact | 75.0 - 140 °C | 167 - 284 °F | Average value: 112 °C Grade Count:37 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:128 |
| Oxygen Index | 20.0 - 37.1 % | 20.0 - 37.1 % | Average value: 24.9 % Grade Count:23 |
| Glow Wire Test | 725 - 960 °C | 1340 - 1760 °F | Average value: 848 °C Grade Count:13 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 280 °C | 446 - 536 °F | Average value: 267 °C Grade Count:10 |
| Nozzle Temperature | 240 - 275 °C | 464 - 527 °F | Average value: 262 °C Grade Count:31 |
| Melt Temperature | 200 - 282 °C | 392 - 540 °F | Average value: 255 °C Grade Count:69 |
| Mold Temperature | 37.8 - 107 °C | 100 - 225 °F | Average value: 72.0 °C Grade Count:72 |
| Ejection Temperature | 170 °C | 338 °F | Average value: 170 °C Grade Count:15 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | Average value: 200 mm/sec Grade Count:17 |
| Drying Temperature | 80.0 - 130 °C | 176 - 266 °F | Average value: 114 °C Grade Count:52 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 4.35 hour Grade Count:40 |
| Moisture Content | 0.0200 - 0.0800 % | 0.0200 - 0.0800 % | Average value: 0.0286 % Grade Count:7 |
| Injection Pressure | 34.5 - 172 MPa | 5000 - 25000 psi | Average value: 95.8 MPa Grade Count:4 |
| Back Pressure | 0.000 - 10.0 MPa | 0.000 - 1450 psi | Average value: 1.17 MPa Grade Count:11 |
| Shot Size | 50.0 - 80.0 % | 50.0 - 80.0 % | Average value: 65.0 % Grade Count:11 |
| Screw Speed | 20.0 - 80.0 rpm | 20.0 - 80.0 rpm | Average value: 59.1 rpm Grade Count:16 |