- 密度 [g/cm3]: 0.0751
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0751 g/cc | 0.00271 lb/in3 | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 2.10 MPa | 305 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.1034 GPa | 15.00 ksi | ISO 527-2, ASTM D 638 |
| Compressive Strength | 1.60 MPa | 232 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Shear Modulus | 0.0276 GPa | 4.00 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 1.00 MPa | 145 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Distortion Resistance; DIN 53424 |