- 密度 [g/cm3]: 0.075
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0750 g/cc | 0.00271 lb/in3 | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 2.80 MPa | 406 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Elongation at Break | 4.5 % | 4.5 % | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.0920 GPa | 13.3 ksi | ISO 527-2, ASTM D 638 |
| Flexural Strength | 2.50 MPa | 363 psi | DIN 53423, ISO 1209, ASTM D 790 |
| Compressive Strength | 1.50 MPa | 218 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Shear Modulus | 0.0290 GPa | 4.21 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 1.30 MPa | 189 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Heat Distortion Resistance; DIN 53424 |