- 拉伸強度 [MPa]: 8.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | °IRHD; ASTM D1415 |
| 105 | 105 | °IRHD, +15 change after 70 hours @ 100°C; ASTM D1415 | |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | -20% change after 70 hours @ 100°C; ASTM D412 |
| 10.0 MPa | 1450 psi | ASTM D412 | |
| Elongation at Break | 60 % | 60 % | -40% change after 70 hours @ 100°C; ASTM D412 |
| 100 % | 100 % | ASTM D412 | |
| Compression Set | 25 % | 25 % | 70 hours @ 100°C; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Minimum Service Temperature, Air | -35.0 °C | -31.0 °F | Non-brittle after 3 minutes |
| -30.0 °C | -22.0 °F | ||
| Flash Point | >= 204 °C | >= 399 °F | |