- 拉伸強(qiáng)度 [MPa]: 42.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 50 cP @Temperature 82.2 °C | 50 cP @Temperature 180 °F | Part A; At processing Temperature |
| 225 cP @Temperature 82.2 °C | 225 cP @Temperature 180 °F | Part B; At Processing Temperature | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 85 | 85 | ASTM D2240 |
| Tensile Strength, Yield | 42.7 MPa | 6200 psi | ASTM D412 |
| Elongation at Break | 800 % | 800 % | ASTM D412 |
| Rebound | 38 % | 38 % | Bashore Rebound; ASTM D 2632 |
| Tear Strength | 83.3 kN/m | 475 pli | Split; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | ASTM D4060 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 82.2 °C | 180 °F | |
| Mold Temperature | 82.2 °C | 180 °F | |
| Cure Time | 30.0 - 40.0 min | 0.500 - 0.667 hour | Demolding Time At 180°F Mold Temperature |
| Pot Life | 2.5 - 3.0 min | 2.5 - 3.0 min | At 180°F Mold Temperature |