- 拉伸強度 [MPa]: 28.19
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 54 | >= 54 | |||
| Tensile Strength, Yield | 28.19 MPa | 4089 psi | |||
| Elongation at Yield | 579 % | 579 % | |||
| 100% Modulus | 0.00190 GPa | 0.276 ksi | |||
| 200% Modulus | 0.00380 GPa | 0.551 ksi | |||
| 300% Modulus | 0.00610 GPa | 0.885 ksi | |||
| Tear Strength | 38.9 kN/m | 222 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 14.0 min @Temperature 68.3 °C | 0.233 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 68.2 | ||||