- 拉伸強度 [MPa]: 27.39
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 66 | >= 66 | |
| Tensile Strength, Yield | 27.39 MPa | 3973 psi | |
| Elongation at Yield | 485 % | 485 % | |
| 100% Modulus | 0.00320 GPa | 0.464 ksi | |
| 200% Modulus | 0.006998 GPa | 1.015 ksi | |
| 300% Modulus | 0.01210 GPa | 1.755 ksi | |
| Tear Strength | 32.6 kN/m | 186 pli | Die C |
| Compression Set | 36.6 % @Temperature 70.0 °C, Time 79200 sec | 36.6 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 12.5 min @Temperature 155 °C | 0.208 hour @Temperature 311 °F | |