- 拉伸強(qiáng)度 [MPa]: 30.1
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 63 | >= 63 | |
| Tensile Strength, Yield | 30.10 MPa | 4365 psi | |
| Elongation at Yield | 568 % | 568 % | |
| 100% Modulus | 0.00250 GPa | 0.363 ksi | |
| 200% Modulus | 0.00540 GPa | 0.783 ksi | |
| 300% Modulus | 0.009398 GPa | 1.363 ksi | |
| Tear Strength | 33.1 kN/m | 189 pli | Die C |
| Compression Set | 35.4 % @Temperature 70.0 °C, Time 79200 sec | 35.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 8.50 min @Temperature 155 °C | 0.142 hour @Temperature 311 °F | |