- 拉伸強(qiáng)度 [MPa]: 29.3
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | |
| Tensile Strength, Yield | 29.30 MPa | 4249 psi | |
| Elongation at Yield | 554 % | 554 % | |
| 100% Modulus | 0.00260 GPa | 0.377 ksi | |
| 200% Modulus | 0.00570 GPa | 0.827 ksi | |
| 300% Modulus | 0.0100 GPa | 1.45 ksi | |
| Tear Strength | 36.4 kN/m | 208 pli | Die C |
| Compression Set | 32.2 % @Temperature 70.0 °C, Time 79200 sec | 32.2 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |