- 拉伸強度 [MPa]: 30.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 60 | >= 60 | |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
| Elongation at Yield | 624 % | 624 % | |
| 100% Modulus | 0.00220 GPa | 0.319 ksi | |
| 200% Modulus | 0.00450 GPa | 0.653 ksi | |
| 300% Modulus | 0.00800 GPa | 1.16 ksi | |
| Tear Strength | 32.5 kN/m | 185 pli | Die C |
| Compression Set | 39.4 % @Temperature 70.0 °C, Time 79200 sec | 39.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 7.50 min @Temperature 155 °C | 0.125 hour @Temperature 311 °F | |