- 拉伸強(qiáng)度 [MPa]: 13.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | |
| Mooney Viscosity | 21 @Temperature 121 °C | 21 @Temperature 250 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 76 | 76 | |
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
| Elongation at Yield | 650 % | 650 % | |
| 100% Modulus | 0.00345 GPa | 0.500 ksi | |
| 300% Modulus | 0.00724 GPa | 1.05 ksi | |
| Tear Strength | 43.0 kN/m | 245 pli | Graves |
| Compression Set | 50 % | 50 % | Method B |
| Processing Properties | Metric | English | Comments |
| Cure Time | 90.0 min @Temperature 142 °C | 1.50 hour @Temperature 287 °F | |