- 拉伸強(qiáng)度 [MPa]: 15.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | |
| Mooney Viscosity | 13 @Temperature 121 °C | 13 @Temperature 250 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 59 | 59 | |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | |
| Elongation at Yield | 725 % | 725 % | |
| 100% Modulus | 0.00241 GPa | 0.350 ksi | |
| 300% Modulus | 0.00569 GPa | 0.825 ksi | |
| Tear Strength | 41.2 kN/m | 235 pli | Graves |
| Compression Set | 72 % | 72 % | Method B |
| Processing Properties | Metric | English | Comments |
| Cure Time | 90.0 min @Temperature 142 °C | 1.50 hour @Temperature 287 °F | |