- 拉伸強(qiáng)度 [MPa]: 18.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | |
| Mooney Viscosity | 20 @Temperature 121 °C | 20 @Temperature 250 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 57 | 57 | |
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
| Elongation at Yield | 450 % | 450 % | |
| 100% Modulus | 0.00190 GPa | 0.275 ksi | |
| 300% Modulus | 0.00362 GPa | 0.525 ksi | |
| Tear Strength | 29.2 kN/m | 167 pli | Graves |
| Compression Set | 24 % | 24 % | Method B |
| Processing Properties | Metric | English | Comments |
| Cure Time | 90.0 min @Temperature 142 °C | 1.50 hour @Temperature 287 °F | |