- 拉伸強(qiáng)度 [MPa]: 26.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | |
| Mooney Viscosity | 67 @Temperature 121 °C | 67 @Temperature 250 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 84 | 84 | |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | |
| Elongation at Yield | 575 % | 575 % | |
| 100% Modulus | 0.00293 GPa | 0.425 ksi | |
| 300% Modulus | 0.00862 GPa | 1.25 ksi | |
| Tear Strength | 58.4 kN/m | 333 pli | Graves |
| Compression Set | 55 % | 55 % | Method B |
| Processing Properties | Metric | English | Comments |
| Cure Time | 90.0 min @Temperature 142 °C | 1.50 hour @Temperature 287 °F | |