- 拉伸強(qiáng)度 [MPa]: 27.64
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |
| Tensile Strength, Yield | 27.64 MPa | 4009 psi | |
| Elongation at Yield | 590 % | 590 % | |
| 100% Modulus | 0.00330 GPa | 0.478 ksi | |
| 200% Modulus | 0.00634 GPa | 0.920 ksi | |
| 300% Modulus | 0.01047 GPa | 1.519 ksi | |
| Tear Strength | 61.5 kN/m | 351 pli | |
| Taber Abrasion, mg/1000 Cycles | 6.0 @Load 1.00 kg | 6.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 42.3 % @Temperature 70.0 °C, Time 79200 sec | 42.3 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |