- 拉伸強度 [MPa]: 17.31
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 | 50 | |
| Tensile Strength, Yield | 17.31 MPa | 2511 psi | |
| Elongation at Yield | 491 % | 491 % | |
| 100% Modulus | 0.00150 GPa | 0.218 ksi | |
| 200% Modulus | 0.00412 GPa | 0.598 ksi | |
| 300% Modulus | 0.007812 GPa | 1.133 ksi | |
| Tear Strength | 42.2 kN/m | 241 pli | Die C |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 160 °C | 0.250 hour @Temperature 320 °F | |