- 拉伸強度 [MPa]: 22.21
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 88 | 88 | |
| Tensile Strength, Yield | 22.21 MPa | 3222 psi | |
| Elongation at Yield | 365 % | 365 % | |
| 100% Modulus | 0.007660 GPa | 1.111 ksi | |
| 200% Modulus | 0.01553 GPa | 2.252 ksi | |
| 300% Modulus | 0.02028 GPa | 2.941 ksi | |
| Tear Strength | 65.7 kN/m | 375 pli | |
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg | 8.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 47.9 % @Temperature 70.0 °C, Time 79200 sec | 47.9 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 154 °C | 0.250 hour @Temperature 309 °F | |