- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.5
- 彎曲強度 [MPa]: 38.0
- 彎曲模量 [MPa]: 1.72
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | ASTM D792 |
| Water Absorption at Saturation | 0.10 % | 0.10 % | 240 hours; Bayer Test |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638/D412 |
| Elongation at Break | 15 % | 15 % | ASTM D638/D412 |
| Flexural Modulus | 1.72 GPa | 249 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Tear Strength | 122 kN/m | 696 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 137 μm/m-°C @Temperature 20.0 °C | 76.1 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Flammability, UL94 | HB @Thickness 3.18 mm | HB @Thickness 0.125 in | |
| HB @Thickness 3.18 mm | HB @Thickness 0.125 in | ||