- 密度 [g/cm3]: 1.04
- 缺口沖擊強度: 6.7
- 彎曲強度 [MPa]: 24.0
- 彎曲模量 [MPa]: 0.350
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0085 cm/cm | 0.0085 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638/D412 |
| Elongation at Break | 200 % | 200 % | ASTM D638/D412 |
| Flexural Modulus | 0.350 GPa | 50.8 ksi | ASTM D790 |
| Izod Impact, Notched | 6.70 J/cm | 12.6 ft-lb/in | ASTM D256 |
| Tear Strength | 90.0 kN/m | 514 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 110 μm/m-°C @Temperature 20.0 °C | 61.1 μin/in-°F @Temperature 68.0 °F | ASTM D696 |