- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 1.1
- 彎曲強度 [MPa]: 35.0
- 彎曲模量 [MPa]: 2.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | ASTM D792 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | 240 hours; Bayer Test |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ASTM D638/D412 |
| Elongation at Break | 22 % | 22 % | ASTM D638/D412 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Tear Strength | 140 kN/m | 799 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 135 μm/m-°C @Temperature 20.0 °C | 75.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |