- 密度 [g/cm3]: 0.95
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.5
- 彎曲強度 [MPa]: 16.0
- 彎曲模量 [MPa]: 0.470
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 - 1.25 g/cc | 0.0343 - 0.0452 lb/in3 | Average value: 1.16 g/cc Grade Count:11 |
| Water Absorption at Saturation | 0.100 - 2.80 % | 0.100 - 2.80 % | Average value: 1.16 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00430 - 0.00750 cm/cm | 0.00430 - 0.00750 in/in | Average value: 0.00607 cm/cm Grade Count:11 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 16.0 - 38.0 MPa | 2320 - 5510 psi | Average value: 27.4 MPa Grade Count:11 |
| Elongation at Break | 15.0 - 200 % | 15.0 - 200 % | Average value: 86.5 % Grade Count:11 |
| Flexural Modulus | 0.470 - 2.07 GPa | 68.2 - 300 ksi | Average value: 1.20 GPa Grade Count:11 |
| Izod Impact, Notched | 0.500 - 4.30 J/cm | 0.937 - 8.06 ft-lb/in | Average value: 1.82 J/cm Grade Count:9 |
| Tear Strength | 70.0 - 140 kN/m | 399 - 799 pli | Average value: 107 kN/m Grade Count:11 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 49.0 - 137 μm/m-°C | 27.2 - 76.1 μin/in-°F | Average value: 75.3 μm/m-°C Grade Count:10 |