- 密度 [g/cm3]: 1.82
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in3 | ASTM D1475 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | Cured property; ASTM D570 |
| Outgassing - Total Mass Loss | 0.45 % | 0.45 % | Cured property; at 10E-6 torr; ASTM E595 |
| Collected Volatile Condensable Material | 0.030 % | 0.030 % | Cured property; at 10E-6 torr; ASTM E-595 |
| Mechanical Properties | Metric | English | Comments |
| Elongation at Break | 70 % @Thickness 0.203 mm | 70 % @Thickness 0.00800 in | Cured; ASTM D638 |
| Tensile Modulus | 0.00517 GPa | 0.750 ksi | ASTM D638 |
| 0.00414 GPa @Temperature 55.0 °C | 0.600 ksi @Temperature 131 °F | ASTM D638 | |
| Shear Strength | 3.45 MPa | 500 psi | Al to Al, 10 mil bondline; ASTM D1002 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 7.00e+14 ohm-cm | 7.00e+14 ohm-cm | Cured property; ASTM D257 |
| Dielectric Constant | 5.8 @Frequency 1000 Hz | 5.8 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Dielectric Strength | >= 39.4 kV/mm @Thickness 0.127 mm | >= 1000 kV/in @Thickness 0.00500 in | Cured; ASTM D149 |
| Dissipation Factor | 0.030 @Frequency 1000 Hz | 0.030 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 μm/m-°C @Temperature 20.0 °C | 22.2 μin/in-°F @Temperature 68.0 °F | Cured property; alpha 1; ASTM E831-86 |
| 160 μm/m-°C @Temperature 20.0 °C | 88.9 μin/in-°F @Temperature 68.0 °F | Cured property; alpha 2; ASTM E831-86 | |
| Thermal Conductivity | >= 1.50 W/m-K | >= 10.4 BTU-in/hr-ft2-°F | |
| Glass Transition Temp, Tg | -75.0 °C | -103 °F | Cured property; ASTM E831-86 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 125 °C | 257 °F | Cure 1 hrs |
| Shelf Life | 4.00 Month | 4.00 Month | at -40°C; JMTP C-100 |